Basalt Roving
Continuous fiber bundles for filament winding, pultrusion and composite production, including pipes, tanks and profiles.
- Linear density
- 110–4,800 tex
- Filament diameter
- 8–24 µm
- Direct modulus
- 88–92 GPa
- Construction
- Direct / assembled
Listed by our production partner. Confirm ordered grade and availability.
Armenian basalt / Quality at the source
Distinctive origins. Measurable quality.
ARMBAS identifies the composition of its Armenian basalt raw material as a foundation for high-quality continuous fiber. The quality case combines the mineral source, fiber-production technology and a specification matched to the application.
Origin alone does not guarantee superior performance. No independent comparison supplied here establishes Armenian basalt as better than every other basalt source. Fiber properties are not finished-composite specifications.
01 / Dimensions & evidence
The specification picture.
Roving properties are not finished laminate or pressure-vessel specifications. Sizing, process settings and application certification need validation.
Roving performance
Roving TDS · p1
| Product / property | Value | Method / scope |
|---|---|---|
| 8–16 µm direct & assembled | >65 cN/tex | Tenacity |
| 17–24 µm direct & assembled | >55 cN/tex | Tenacity |
| Assembled ≤600 tex | 3,000–3,200 MPa | ASTM D2343 |
| Assembled ≥800 tex | 2,900–3,100 MPa | ASTM D2343 |
| Direct tensile strength | 2,900–3,200 MPa | ASTM D2343 |
| Assembled tensile modulus | 86–90 GPa | ASTM D2343 |
| Direct tensile modulus | 88–92 GPa | ASTM D2343 |
| Elongation at break | 3.5% | Supplier value |
| Density | 2.63 g/cm³ | DIN 65569 |
| Moisture, all sizing | <0.1% | Supplier value |
| Loss on ignition | Typically >0.4% | Sizing-dependent |
| Filament diameter | 8–24 µm | Range |
| Linear density | 110–4,800 tex | Range |
Roving construction & packing
Roving TDS · p1
| Property | Direct | Assembled |
|---|---|---|
| Construction | Untwisted continuous strand | Several strands combined |
| Unwinding | Internal only | External / internal |
| Product code | ABFR-D-I-14-400-KV42 | D direct; RA regular assembled; CA customized assembled; I internal; E external |
| Sizing | Silane-based; resin compatibility on request | Silane-based; resin compatibility on request |
| Bobbin height | 255 mm | Internal 255 mm; external 270 mm |
| Inner diameter | 160 mm | Internal 80 mm; external 76 mm cardboard core |
| Bobbin weight | 3–18 kg, tex-dependent | External 8 kg; internal 9 kg |
| Pallet load | Up to 850 kg | Up to 850 kg |
| Packaging | Shrink film, cardboard box, euro pallet / 100 × 120 cm pallet | Same |
02 / In practice
From material to application.
Winding & pultrusion
Continuous fiber feedstock for resin-bound pipes, tanks and profiles.
Weaving & composite manufacture
Roving can be converted into reinforcement fabrics; sizing must match the resin and process.
03 / Economic value
Evaluate the whole life.
Compare fiber price with resin use, processing yield and cycle time. Raw-fiber strength alone does not determine finished-part cost.
Purchase · freight · installation · maintenance · downtime · replacement. No guaranteed savings or lifespan.
04 / Your project
The right grade.
For your application.
Include required dimensions, quantity, use and delivery location. Materials ship directly from Armenia when confirmed with our production partner.